At present, the tin- mineral mines produced by various countries' tin- smelting plants are smelted by using tin alloys with higher grades in a matching manner. China has a large number of containing arsenic, antimony high refractory tin, so the late 1970s made many experimental studies. Sulfur vulcanization is very effective in enriching tin, so the process of combining metallurgy and metallurgy is adopted. In the beneficiation process, only a complex tin ore containing arsenic and antimony is produced to increase the recovery rate of tin, and then the complex tin ore is vulcanized in a fumigating furnace to obtain a complex tin soot.
Figure 1 Tin-making process of top converter in Texas Tin Refinery
The handling of complex tin soot is still in the experimental stage and there are several different processes.
One of the processes is shown in Figure 3. The chemical composition (%) of tin used in the test was: 4.96Sn, 4.33Pb, 3.15Sb, 1.77As, 0.025Ag, 0.011In, 0.019Cd, 0.30Cu, 5.99S, 0.30C, 28.95Fe, 0.88CaO, 20.44 SiO 2 , 3.05Al 2 O 3 , the product is sodium stannate.
Figure 2 Siro melting furnace system combination diagram
The second process is shown in Figure 4. The chemical composition (%) of the tin soot used in the test was: 21.26Sn, 17.92Pb, 9.73As, 12.56Sb, 5.03Zn, 0.041Ag, 0.047In, 0.19Cd, 3.79S, 2.63Fe, 0.29CaO, 3.28SiO 2 . The phase analysis is shown in the table below. Tin-lead alloy products.
Phase analysis of high arsenic and antimony metal tin soot in the table /%
tin
lead
arsenic
antimony
Zinc
Phase
content
Phase
content
Phase
content
Phase
content
Phase
content
SnO
SnO 2
Sn
5.7
87.9
6.2
PbSO 4
PbO
PbS
Insoluble slag
25.1
57.1
5.5
11.7
As 2 O 3
M3(AsO 4 ) 2
As
As 2 S 3
32.3
57.5
1.9
8.3
Sb 2 O 3
Sb 2 S 3
M3(SbO 4 ) 2
21.6
4.3
74.1
ZnO
ZnS
Insoluble slag
6.2
84.8
0.9
[next]
Figure 3 complex tin soot smelting - alloy plus alkali smelting - alkali slag flooding
- Leachate purification and concentration process for producing sodium stannate
The third process is shown in Figure 5. The chemical composition (%) of the sample was: 23.28Sn, 11.81Sb, 20.74Pb, 4.79Zn, 0.055Ag, 2.56S, 6.42As, 1.85Fe, 0.004Bi, 0.81CaO, 2.79SiO 2 , 2.79SiO 2 , 1.20Al 2 O 3 , 0.047In. This is a combination of wet and fire method. The chlorination reduction leaching method is used to completely separate arsenic at one time; and the associated elements such as bismuth, lead, zinc, silver and iron can be completely removed, and then enter the traditional Fire process.
Figure 4: High arsenic bismuth polymetallic tin soot reduction roasting (twice) arsenic removal 锑
Reduction smelting- electrolytic refining process for producing tin-lead alloy
Figure 5 CR (chlorination reduction leaching distillation) treatment
Principle process of high arsenic and antimony metal tin soot

Knit Dress

Knit Dress
The Knit Dress are different from ordinary skirts. As the name suggests, they are skirts made of knitted materials, using knitting needles to form loops of various raw materials and yarns, and then stringing them into a form of skirt. Knitted skirts are popular among women in autumn and winter, because they can show feminine beauty while keeping warm. It will not look bloated even if you wear thick warm pants inside, so it has become the most popular clothing in recent years.

Yacheng Knitting Co., Ltd. can mass produce customized high-quality knitted garments, including sweaters, Custom Knit Sweaters, Knitted Pants, Knitted Skirt, Knitted Shoes, Knitted Scarves and Knitting Blanket. If you need to order knitted products, please contact us.

Knit Dress

Knit Dress,Knit Sweater Dress,Women Knit Dress,Knitted Jumper Dress

DongGuan Yacheng Knitting Co., Ltd , https://www.oemknittingycs.com